| 超导Tl2Ba2CaCu2O8+x 薄膜的太赫兹复电导率的提取 |
|
管云1, 邢建2, 季鲁2, 吴敬波1, 金飚兵1
|
|
|
| (1.南京大学电子科学与工程学院超导电子学研究所, 南京,210023;2.南开大学电子信息与光学工程学院, 天津,300350) |
|
| 摘要: |
| 采用低温太赫兹时域光谱系统, 测试了高温超导 Tl2Ba2CaCu2O8+x 薄膜的太赫兹透射谱, 并提取了它在不同温度下的太赫兹电导率. 研究过程中发现提取后的参数存在电导率随频率波动大、与理论值偏差较大等问题.通过对基片厚度和太赫兹波入射角度的误差对高温超导薄膜电导率的影响进行了分析, 结果表明导致数据波动大是由于基片厚度的偏差引起的. 针对厚度差的影响, 一种矫正方法被提出, 通过对厚度的修正, 提高了数据提取的质量. |
| 关键词: 太赫兹时域光谱技术, 高温超导薄膜, 太赫兹电导率, 数据提取的不确定性 |
| DOI：10.13380/j.ltpl.2019.02.009 |
|
| 基金项目: |
|
| The Extraction of Terahertz Complex Conductivity of Superconducting Tl2Ba2CaCu2O8+x Film |
|
GUAN Yun1, XING Jian2, JI Lu2, WU Jingbo1, JIN Biaobing1
|
| (1.Research Institute of Superconductor Electronics , Nanjing University , Nanjing , 210023;2.College of Electronic Information and Optical Engineering , Nankai University , Tianjin 300350, China) |
| Abstract: |
| The transmission spectra of the high-temperature superconducting Tl2Ba2CaCu2O8+x (TBCCO) films were measured using terahertz(THz) time domain spectroscopy(TDS) , and the THz conductivities at different temperatures were extracted. It is found that the extracted complex conductivity has some problems, such as the large fluctuation of the conductivity with frequency and large deviation from theoretical values. Based on the analysis on how the errors of the substrate thickness and the incident angle of the THz wave affect the extracted complex conductivity of the TBCCO films, itisshownthatthelargefluctuationoftheconductivityiscausedbytheerrorof the substrate thickness. Aiming at eliminating influence of the error of the substrate thickness, a correction method is proposed. Through the correction of the substrate thickness, the extracted complex conductivity of the TBCCO films gain great improvement. |
| Key words: Terahertz time domain spectroscopy, High-temperature superconducting films, Complex conductivity in THz region, Uncertainty in data extraction |